钢号

C

Si

Mn

P≤

S≤

Cr

Mo

Ni

其它

SUS201

≤0.15

≤1.00

5.5-7.5

0.06

0.03

16-18

-

3.5-5.5

N≤0.25

202

≤0.15

≤1.00

7.5-10.0

0.06

0.03

17-19

-

4.0-6.0

N≤0.25

301

≤0.15

≤1.00

≤2.00

0.045

0.03

16-18

-

6.0-8.0

-

302

≤0.15

≤1.00

≤2.00

0.045

0.03

17-19

-

8-10.0

-

303

≤0.15

≤1.00

≤2.00

0.2

≥0.015

17-19

≤0.6

8.0-10.0

-

304

≤0.08

≤1.00

≤2.00

0.045

0.03

18-20

-

8-1.0.5

-

304L

≤0.03

≤1.00

≤2.00

0.045

0.03

18-20

-

9-13

-

305

≤0.12

≤1.00

≤2.00

0.045

0.03

17-19

-

10.5-13

-

309S

≤0.08

≤1.00

≤2.00

0.045

0.03

22-24

-

12-15

-

310S

≤0.08

≤1.5

≤2.00

0.045

0.03

24-26

-

19-22

-

316

≤0.08

≤1.00

≤2.00

0.045

0.03

16-18

2-3

10-14

-

316L

≤0.03

≤1.00

≤2.00

0.045

0.03

16-18

2-3

12-15

-

317

≤0.08

≤1.00

≤2.00

0.045

0.03

18-20

3-4

11-15

-

317L

≤0.03

≤1.00

≤2.00

0.045

0.03

18-20

3-4

11-15

-

321

≤0.08

≤1.00

≤2.00

0.045

0.03

17-19

-

9-13

Ti≥5×C

405

≤0.08

≤1.00

≤1.00

0.04

0.03

11.5-14.5

-

≤0.6

AL0.1-0.3

420F

0.26-0.4

≤1.00

≤1.25

0.06

≥0.15

12-14

≤0.6

≤0.6

-

430

≤0.12

≤0.75

≤1.00

0.04

0.03

16-18

-

≤0.6

-

 2Cr25Ni20

承受1035℃以下反复加热的抗氧化钢。炉用部件、喷嘴、燃烧室

 1Cr18Ni9Ti

有良好的耐热性及抗腐蚀性。作加热炉管、燃烧室简体，遭火炉罩

 0Cr17Ni12Mo2

高温具有优良的蠕变强度，作热交换用部件，高温耐蚀类螺拴

 0Cr25Ni20

比0Cr23Nil3抗氧化性好，可承受1235℃加热。炉用材料，汽车净化装置用材料

 2Cr23Ni13

承受980℃以下反复加热的抗氧化钢。加热炉部件，重油燃烧器

 0Cr19Ni9

通用耐氧化钢，可承受870℃以下反复加热

 0Cr18Ni11Ti

作在400～900℃腐蚀条件下使用的部件，高温用焊接结构部件

 0Cr18Ni11Nb

作在400～900℃腐蚀条件下使用的部件，高温用焊接结构部件

 5Cr21Mn9Ni4N

以经受高温强度为主的汽油及柴油机用排气阀

 Y5Cr21Mn9Ni4N

以经受高温强度为主的汽油及柴油机用排气阀

 2Cr22Ni11N

以抗氧化为主的汽油及柴油机用排气闽