Inconel600 (UNS6600)
|
|
Inconel600 Features and application areas overview：
|
|
The alloy is a nickel-chromium-iron-based solid solution strengthening alloy with good high temperature corrosion and oxidation resistance, excellent hot and cold processing and welding properties, with satisfactory thermal strength and high plasticity below 700 ℃. The alloy can be strengthened by cold working, but also by resistance welding, soldering or brazing. It is suitable for producing anti-oxidation parts under 1100 ℃ under low load.
|
|
Inconel600 Similar brand：
|
|
GH600 (China) NC15FE (France), W.Nr.2.4816 NiCr15Fe (Germany) NA14 (UK)
|
|
Inconel600 chemical composition：
|
|
Alloy
牌号
|
%
|
Ni
Ni
|
Co
Co
|
Cr
Cr
|
Fe
Fe
|
Nb
Nb
|
Ta
Ta
|
C
C
|
Mn
Mn
|
Si
Si
|
S
S
|
P
P
|
Cu
Cu
|
Ai
Al
|
Ti
Ti
|
|
Inconel
600
|
Min
|
|
|
14
|
6.0
|
|
|
|
|
|
|
|
|
|
|
|
Max
|
72
|
17
|
10.0
|
1.0
|
0.15
|
1.0
|
0.5
|
0.015
|
0.04
|
0.5
|
0.35
|
0.50
|
|
|
Inconel600 Physical Properties：
|
|
Density
g/cm3
|
Melting point
℃
|
Thermal conductivity
λ/(W/m•℃)
|
Specific heat capacity
J/kg•℃
|
Elastic Modulus
GPa
|
Shear modulus
GPa
|
Resistivity
μΩ•m
|
Poisson's ratio
|
Linear expansion coefficient
a/10-6℃-1
|
|
8.43
|
1370
1430
|
12.85(100℃)
|
435
|
205
|
76
|
1.05
|
0.34
|
12.35(20~100℃)
|
|
|
Inconel600 Mechanical properties: (at 20 ℃ minimum mechanical properties testing)
|
|
Heat treatment methods
|
Tensile strengthσb/MPa
|
Yield Strengthσp0.2/MPa
|
Elongationσ5 /%
|
Brinell hardness HBS
|
|
Solution treatment
|
585
|
240
|
30
|
≥217
|
|
|
Inconel600 Production standards：
|
|
Standard
|
Bar
|
Forgings
|
Plate (with) material
|
Wire
|
Pipe
|
|
American Society for Testing and Materials
|
ASTM B166
|
ASTM B166
|
ASTM B168
|
ASTM B166
|
ASTM B167
ASTM B163
ASTM B516
ASTM B517
|
|
American Aerospace Materials Technical Specification
|
AMS 5665
|
AMS 5665
|
AMS 5540
|
AMS 5687
|
AMS 5580
|
|
American Society of Mechanical Engineers
|
ASME SB166
|
ASME SB166
|
ASTM SB168
|
ASME SB166
|
ASME SB167
ASTM SB163
ASTM SB516
ASTM SB517
|
|
|
Inconel600 Metallographic structure：
|
|
The alloy was treated at 1120 ℃ for 2h, only TiN nitride and Cr7C3 carbide remained Cr7C3 and TiN in the microstructure after being aged at 870 ℃ for 1 000 ℃, indicating that the microstructure of the alloy is stable
。
|
|
Inconel600 Process performance and requirements：
|
|
1, the alloy has good thermal processing properties, steel forging heating temperature 1110 ℃ ~ 1140 ℃.
2, the average grain size of the alloy and forging deformation degree, the final forging temperature is closely related.
3, the alloy has good welding performance, the original arc welding, welding, resistance welding and brazing and other methods of connection, large or complex welding structure after welding at 870 ℃ annealing 1h, to eliminate welding stress.
4, the alloy shall be machined after heat treatment, due to material hardening, it is appropriate to use lower than the standard machining of low-alloy austenitic stainless steel cutting speed and heavy knife for processing, to car into the hardened surface below . surface.
|